NACE CIP 2 Study Guides Exam Questions With
Correct Answers
What |is |the |cause |of |chalking |in |epoxy |coating |- |CORRECT |ANSWER✔✔-UV |or |radiation |
exposure
What |is |polymerization |cured |coating? |- |CORRECT |ANSWER✔✔-Two |parts |mixed |together |just |
prior |to |use
Examples |of |non-convertible |coatings |- |CORRECT |ANSWER✔✔-1. |Chlorinated |rubber |2. |Vinyl |
3. |Acrylic |4. |Bituminous
Non-convertible |curing |def. |- |CORRECT |ANSWER✔✔-No |chemical |change |during |cure |cycle
Convertible |curing |def. |- |CORRECT |ANSWER✔✔-Some |chemical |change |during |cure |cycle
What |info |should |be |included |when |sending |samples |to |a |lab? |- |CORRECT |ANSWER✔✔-1. |
Identity |of |materials |2. |Properly |packed/labeled |samples |3. |Chain |of |custody |form |4. |Type |of |
analysis |that |is |expected |and |the |concentrations |of |interest
Specialized |tests |or |equipment |coating |inspectors |may |encounter |- |CORRECT |ANSWER✔✔-1. |
AA/AE |Atomic |Absorption/Emission |2. |ISP |Induction |coupled |plasma |Spectrometer |3. |GLC |Gas |
liquid |chromatographs |4. |IR, |FTIR, |FTIR-ATR |INfrared |spectrophotometers |5. |DSC |Differential |
scanning |calorimeters
What |is |a |cathodic |dis-bondment |test? |- |CORRECT |ANSWER✔✔-Procedure |to |determine |how |
easily |a |coating |loosens |from |a |substrate |or |develops |holidays |as |a |result |of |normal |soil |
potentials
, Individuals |who |perform |surveys |- |CORRECT |ANSWER✔✔-1. |O-Cat |or |S-cat |tech |2. |NACE |
coating |specialist |3. |NACE |Level |III |4. |Coating |Inspector |w/field |experience |5. |Coating |
manufacturer |representative |6. |Maintenence |engineer |with |specific |plant |knowledge.
Coating |survey |steps |- |CORRECT |ANSWER✔✔-1. |Understand |scope |2. |Gather |team |3. |Develop |
survey |plan |4. |Review |standards |5. |Agree |on |format |6. |Delegate |various |tasks |7. |Eveluate |
existing |coating |8. |Delegate |various |tasks |9. |Evaluate |existing |coating |10. |Gather |additional |
info |11. |Summarize |data |12. |Prepare |maintenance |plans |13. |Prepare |reports/input |data |14. |
Submit |final |survey |reports.
List |some |of |the |primary |reasons |surveys |are |performed |- |CORRECT |ANSWER✔✔-1. |Plan |
maintenance. |2. |Prioritize |work |3. |Budgetary |concerns |4. |Determine |value |of |assets |5. |Legal |
compliance
Definition |of |a |coating |survey |- |CORRECT |ANSWER✔✔-Gather |baseline |info |needed |to |plan |
maintenance |coating |procedures
What |are |faying |surfaces |and |why |not |galvanize |them? |- |CORRECT |ANSWER✔✔-Surfaces |that |
depend |on |friction |to |hold |galvanizing |it |may/will |reduce |friction |if |they |are |galvanized
Common |problems |seen |during |the |usual |inspections |of |HD |galvanized |items |- |CORRECT |
ANSWER✔✔-1. |Cracking |2. |Peeling |3. |Bare |spots |4. |Lumps |5. |Blisters |6. |Flux |inclusions |7. |Ash |
inclusions |8. |Dross |inclusions
Post |galvanizing |treatments |and |why |- |CORRECT |ANSWER✔✔-To |Remove |Thickness: |Roll, |
Wipe, |Centrifuge/Air |Blast
To |change |properties/To |alloy: |Annealing
Temperature |range |for |galvanizing |kettle |- |CORRECT |ANSWER✔✔-820-850 |F
Correct Answers
What |is |the |cause |of |chalking |in |epoxy |coating |- |CORRECT |ANSWER✔✔-UV |or |radiation |
exposure
What |is |polymerization |cured |coating? |- |CORRECT |ANSWER✔✔-Two |parts |mixed |together |just |
prior |to |use
Examples |of |non-convertible |coatings |- |CORRECT |ANSWER✔✔-1. |Chlorinated |rubber |2. |Vinyl |
3. |Acrylic |4. |Bituminous
Non-convertible |curing |def. |- |CORRECT |ANSWER✔✔-No |chemical |change |during |cure |cycle
Convertible |curing |def. |- |CORRECT |ANSWER✔✔-Some |chemical |change |during |cure |cycle
What |info |should |be |included |when |sending |samples |to |a |lab? |- |CORRECT |ANSWER✔✔-1. |
Identity |of |materials |2. |Properly |packed/labeled |samples |3. |Chain |of |custody |form |4. |Type |of |
analysis |that |is |expected |and |the |concentrations |of |interest
Specialized |tests |or |equipment |coating |inspectors |may |encounter |- |CORRECT |ANSWER✔✔-1. |
AA/AE |Atomic |Absorption/Emission |2. |ISP |Induction |coupled |plasma |Spectrometer |3. |GLC |Gas |
liquid |chromatographs |4. |IR, |FTIR, |FTIR-ATR |INfrared |spectrophotometers |5. |DSC |Differential |
scanning |calorimeters
What |is |a |cathodic |dis-bondment |test? |- |CORRECT |ANSWER✔✔-Procedure |to |determine |how |
easily |a |coating |loosens |from |a |substrate |or |develops |holidays |as |a |result |of |normal |soil |
potentials
, Individuals |who |perform |surveys |- |CORRECT |ANSWER✔✔-1. |O-Cat |or |S-cat |tech |2. |NACE |
coating |specialist |3. |NACE |Level |III |4. |Coating |Inspector |w/field |experience |5. |Coating |
manufacturer |representative |6. |Maintenence |engineer |with |specific |plant |knowledge.
Coating |survey |steps |- |CORRECT |ANSWER✔✔-1. |Understand |scope |2. |Gather |team |3. |Develop |
survey |plan |4. |Review |standards |5. |Agree |on |format |6. |Delegate |various |tasks |7. |Eveluate |
existing |coating |8. |Delegate |various |tasks |9. |Evaluate |existing |coating |10. |Gather |additional |
info |11. |Summarize |data |12. |Prepare |maintenance |plans |13. |Prepare |reports/input |data |14. |
Submit |final |survey |reports.
List |some |of |the |primary |reasons |surveys |are |performed |- |CORRECT |ANSWER✔✔-1. |Plan |
maintenance. |2. |Prioritize |work |3. |Budgetary |concerns |4. |Determine |value |of |assets |5. |Legal |
compliance
Definition |of |a |coating |survey |- |CORRECT |ANSWER✔✔-Gather |baseline |info |needed |to |plan |
maintenance |coating |procedures
What |are |faying |surfaces |and |why |not |galvanize |them? |- |CORRECT |ANSWER✔✔-Surfaces |that |
depend |on |friction |to |hold |galvanizing |it |may/will |reduce |friction |if |they |are |galvanized
Common |problems |seen |during |the |usual |inspections |of |HD |galvanized |items |- |CORRECT |
ANSWER✔✔-1. |Cracking |2. |Peeling |3. |Bare |spots |4. |Lumps |5. |Blisters |6. |Flux |inclusions |7. |Ash |
inclusions |8. |Dross |inclusions
Post |galvanizing |treatments |and |why |- |CORRECT |ANSWER✔✔-To |Remove |Thickness: |Roll, |
Wipe, |Centrifuge/Air |Blast
To |change |properties/To |alloy: |Annealing
Temperature |range |for |galvanizing |kettle |- |CORRECT |ANSWER✔✔-820-850 |F